HELLTECH FLOOR EPOXY SELF LEVELLING-F Multi Functional Phenolic Based Epoxy Coating Compound

HELLTECH FLOOR EPOXY SELF LEVELLING-F

Multi Functional Phenolic Based Epoxy Coating Compound

Description

It is an phenolic epoxy resin-based, two-component, solvent free and color flooring of low viscosity, which is used as self levelling multilayer or thin coat coating when mixed with proper filling materials.

Usage

It is used on the concrete, cement or epoxy mortars for all industrial floors:
High chemical resistance where needed in the warehouse, hangar and repair-maintenance units,
For epoxy multilayer systems applicable at the factories,worksops,production and packaging sites having a traffic of forklift, loader and heavy vehicles
On surfaces subject to medium to heavy load in many places which require mechanical, chemical and wear resistance by mixing silica sand or different fillers.

Advantages

Characteristics

Finish	: Semi-gloss
Color	: Any colors
Density	: 1,4 ± 0,05 kg/lt (A+B)
Mix Ratio	: 4:1 (A:B – by weight)
Solids by Volume	: %100 (A+B)
Pot Life (+10°C)	: 60 minutes
(+30°C)	: 40 minutes
Wait Time Between Coats	: 14-16 hours / at 20°C
Ready for Light Traffic	: 24 hours / at 20°C
Full Cure	: 7 days / at 20°C
VOC	: 0 gr/ml
Compression Strength	: 60 N/mm² (in full cure)
Taber Abrasion Resistance	:50 mg (in full cure)
Flexural Strength	:35 N/mm² (in full cure)

Physical characteristics are for the mixture of 1 part Novatech Epoxy Self Levelling-F and 1 part quarts sand.

Application

Mixing Procedure

It is a two-component product and it should, therefore, be propared at the mix ratio specified for the quantity to be used, taking into consideration the pot life. For a homogenous mixture, make sure that the product temperature should not be less than 15°C. Component A should be stirred by itself by use of a mechanical mixer quickly and then the hardener (Component B) should be added, taking care of the mix ratio. Components A and B should be stirred for minimum 3 minutes until you have a homogenous mixture.

Surface Application

After made ready to apply, the mixture is preferably applied by toothed trowel in amount specified in the paint system or in such amount to obtain he desired dyr film thickness as controlled by wet film comb. Wait time between the coats is minimum 24 hours (20°C) and maximum 5 days. It is very important that the second coat should be applied within the time for overcoating specified above. Air bubbles of the fresh coat thoroughly spread over the surface should be eliminated. (Special care should be shown for it in case of applications of 1 kg/m2 or above 700 microns.) It reaches to a full mechanical and chemical strength in about 7 days.

Packaging

Storage

Consumption

SAMPLE SYSTEM 1: (High chemical resistance where needed in the warehouse, hangar and repair-maintenance units – 2,0-2,5mm)

As impregnation of the concrete surface:

HELLTECH FLOOR /NOVATECH FLOOR EP OXY SEALER 5000 : 150-200 g/m2
(For better impregnation, it is recommended to thin it with Epoxy Thinner by 10-20% depending on the surface of the concrete)

As base coat :

HELLTECH FLOOR / NOVATECH FLOOR EPOXY MORTAR SL : 2000-2500 gr/m2

As a top coat :

HELLTECH FLOOR / NOVATECH FLOOR EPOXY SELF LEVELLİNG-F : 1500 gr/m2

SAMPLE SYSTEM 2 : Factories,workshops,production and packaging sites having a traffic of forklift, loader and heavy vehicles – 1,0 mm suitable for use

As impregnation of the concrete surface:

HELLTECH FLOOR / NOVATECH FLOOR E POXY SEALER 5000 : 300-400 g/m2
(For better impregnation, it is recommended to thin it with Epoxy Thinner by 10-20% depending on the surface of the concrete)

As a top coat :

HELLTECH FLOOR / NOVATECH FLOOR EPOXY SELF LEVELLİNG-F : 1500 gr/m2