It is an epoxy resin-based, two-component, solvent-free and colorflooring of low viscosity, which is used as self levelling multilayer or thin coat coating when mixed with proper filling materials.
- It is used on the concrete, cement or epoxy mortars for all industrial floors;
- In the warehouse, hangar and repair-maintenance units,
- For epoxy multilayer systems applicable at the factories, workshops , production and packaging sites having a traffic of forklift, loader and heavy vehicles
- On surfaces subject to medium to heavy load in many places which require mechanical, chemical and wear resistance by mixing silica sand or different fillers.
- Solvent-free, low viscosity, resilient structure,
- High wetting capability,
- High compression and wear resistance,
- Easy to clean and resistant to chemicals
Finish | : Gloss |
Color | : Any colors |
Density | :1,4 ± 0,05 kg/lt (A+B) |
Mix Ratio | : 4:1 (A:B – by weight) |
Solids by Volume | : 100% (A+B) |
Pot Life (+10°C) | : 50 minutes |
(+30°C) | : 20 minutes |
Wait Time Between Coats | : 24 hours / at 20°C |
Ready for Light Traffic | : 24 hours / at 20°C |
Full Cure | : 7 days / at 20°C |
Compression Strength | : 60 N/mm² (in full cure) |
Taber Abrasion Resistance | : 50 mg (in full cure) |
Flexural Strength | : 35 N/mm² (in full cure) |
Mixing Procedure
It is a two-component product and it should,therefore, be prepared at the mix ratio specified for the quantity to be used, taking into consideration the pot life. For a homogenous mixture, make sure that the product temperature should not be less than 15°C. Component A should be stirred by itself by use of a mechanical mixer quickly and then the hardener (Component B) should be added, taking care of the mix ratio. Components A and B should be stirred for minimum 3 minutes until you have a homogenous mixture.
Surface Application
After made ready to apply, the mixture is applied with toothed trowel on the surface primed and levelbalanced for self-levelling flooring. Air bubbles of he fresh flooring that spreads over the surface thoroughly should be removed by spiked roller. Roller is used for thin coating. Wait time between the coats is minimum 24 hours (20°C) and maximum 5 days. It is very important that the second coat should be applied within the time for overcoating specified above. Lt reaches to a full mechanical and chemical strength in about 7 days.
Cleaning Of Tools
Cellulosic or Epoxy thinner.
A 13,5-kg set of HELLTECH FLOOR NOVATECH FLOOR EPOXY SEALER 5005 consists of Component A in one pail of net 10 kg and Component B in one gallon of net 3,5 kg.
Store the product in a cool and dry place. Shelf life of the product is 1 year for Components A and B when stored properly in the original container unopened.
As impregnation primer :
100-400 g/m2 (Depending on the concrete surface, it is recommended to thin it with Epoxy Thinner by
5-10 % for better impregnation)
Level stabilization mortar :
HELLTECH FLOOR / NOVATECH FLOOR EPOXY SEALER 5005 : 500 gr/m2
0,1 – 0,3 mm quartz sand : 500 gr/m2
6-7 mm epoxy mortar :
HELLTECH FLOOR / NOVATECH FLOOR EP OXY S E A L E R 5 0 0 5 : 1,5 kg/m2
0,1 – 0,6 mm quartz sand : 4,8 kg/m2
0,6 – 2,0 mm quartz sand : 7,2 kg /m2
Related products
Company
Parquet Products
Waterproof Products
Contact Information
Head Office Address
Orucreis Mah.Tekstilkent Cad. No: 10V Blok No:214 (2. Kat) Tekstilkent Ticaret Merkezi Esenler / ISTANBUL / TURKEY
Factory Address
Buyukbakkalkoy Mahallesi Yakacik Yolu Sokak No: 2/1 Merkez
Maltepe / ISTANBUL / TURKEY