It is a polyester polyurethane resin-based, two-component, free-solvent, resilient and color flooring of self-levelling which is used as multilayer or thin layer.
- Self-levelling flooring in thickness of 1-3mm at sport fields,
- For exhibition and fair halls and offices subject to light pedestrian and vehicle traffic,
- For hospitals, polyclinics, laboratory, playpens, kindergartens, poultry hatcheries and slaughter houses which require hygienic conditions.
- Forms a monolithic flooring which does not reqire joint,
- Hygienic and healthy,
- Easy to clean. It can be cleaned by detergent and cleaning agents containing solvent,
- Forms a semi-gloss surface, and
- Wear and skid resistant.
Finish | : Gloss |
Color | :Gray, Beige, Oxide red |
Density | : 1,40 ± 0,05 kg/lt (A+B / 20°C de) |
Mix Ratio | : 16:3,5 (A:B – by weight) |
Solids by Volume | : %100 (A+B) |
Pot Life (+10°C) | : 60 minutes |
(+30°C) | : 40 minutes |
Wait Time Between Coats | |
(+10°C) | : 24 hours / at 20°C |
(+20°C) | : 12 hours / at 20°C |
Ready for Light Traffic | : 7 days / at 20°C |
Full Cure | : 7 days / at 20°C |
Shore A Hardness | : 80 |
Elongation at Break | : %120 /at 20°C |
Breaking Strength | : 115 kg/cm² |
Taber Abrasion Resistance | : 20 mg (in full cure) |
These are typical values and there may be deviations.
Mixing Procedure
It is a two-component product and it should, therefore, be propared at the mix ratio specified for the quantity to be used, taking into consideration the pot life. For a homogenous mixture, make sure that the product temperature should not be less than 15°C. Component A should be stirred by itself by use of a mechanical mixer quickly and then the hardener (Component B) should be added, taking care of the mix ratio. Components A and B should be stirred for minimum 3 minutes until you have a homogenous mixture.
Surface Application
After made ready to apply, the mixture is preferably applied by toothed trowel in amount specified in the paint system or in such amount to obtain he desired dyr film thickness as controlled by wet film comb. Wait time between the coats is minimum 24 hours (20°C) and maximum 5 days. It is very important that the second coat should be applied within the time for overcoating specified above. Air bubbles of the fresh coat thoroughly spread over the surface should be eliminated. (Special care should be shown for it in case of applications of 1 kg/m2 or above 700 microns.) It reaches to a full mechanical and chemical strength in about 7 days.
Material Consumption
Quantity of Novatech floor 3025 to form a coating in thickness of 1 mm over an area of 1 m² is between 1,4-1,5 kg.
Clean Up
Cellulosic or Polyurethane thinner.
A 19.5-kg set of HELLTECH FLOORNOVATECH FLOOR 3025 consists of Component A in one pail of net 16 kg and Component B in one galloon of net 3.5 kg.
Store the product in a cool and dry place. Shelf life of the product is 1 year for Components A and B when stored properly in the original container unopened.
As impregnation of the concrete surface:
HELLTECH FLOOR / NOVATECH FLOOR EP OXY SEALER 5000 : 100-200 g/m2
(For better impregnation, it is recommended to thin it with Epoxy Thinner by 10-20% depending on the
surface of the concrete)
As bearing layer:
SBR Rubber (in thickness of 6-10 mm)
As pore filler on the bearing layer :
HELLTECH FLOOR / NOVATECH FLOOR POR 4065 : 400-500 gr/m2
As resilient base coat :
HELLTECH FLOOR / NOVATECH FLOOR 3025 : 2000–2500 gr/m2
As color topcoat :
HELLTECH FLOOR / NOVATECH FLOOR PUR TOPCOAT SPORT MATT : 100-150 gr/m2
Related products
Company
Parquet Products
Waterproof Products
Contact Information
Head Office Address
Orucreis Mah.Tekstilkent Cad. No: 10V Blok No:214 (2. Kat) Tekstilkent Ticaret Merkezi Esenler / ISTANBUL / TURKEY
Factory Address
Buyukbakkalkoy Mahallesi Yakacik Yolu Sokak No: 2/1 Merkez
Maltepe / ISTANBUL / TURKEY